Material Grades
Nickel Alloy Grades
Fastener Nickel Alloy Grades and Duplex Stainless Steel Grades, filter through their mechanical and chemical compositions below
Filter By
INCONEL 600
Chemical compositions and mechanical properties for INCONEL 600.
Chemical compositions - INCONEL 600
Element | % Present |
---|---|
Carbon (C) | 0.07 |
Chromium (Cr) | 17.50 - 19.50 |
Manganese (Mn) | 2 |
Silicon (Si) | 1 |
Phosphorous (P) | 0.045 |
Sulphur (S) | 0.015b |
Nickel (Ni) | 8.00 - 10.50 |
Nitrogen (N) | 0.1 |
Iron (Fe) | Balance |
Mechanical properties - INCONEL 600
Element | % Present |
---|---|
Carbon (C) | 0.03 |
Chromium (Cr) | 17.50 - 19.50 |
Manganese (Mn) | 2 |
Silicon (Si) | 1 |
Phosphorous (P) | 0.045 |
Sulphur (S) | 0.015b) |
Nickel (Ni) | 8.00 - 10.50 |
Nitrogen (N) | 0.1 |
Iron (Fe) | Balance |
INCONEL 625
Chemical compositions and mechanical properties for INCONEL 625.
Chemical compositions - INCONEL 625
Property | Value |
---|---|
Comprehensive Strength | 210 MPa |
Proof Stress | 210 Min MPa |
Tensile Strength | 520 - 720 MPa |
Elongation | 45 Min% |
Mechanical properties - INCONEL 625
Property | Value |
---|---|
Proof Stress | 200 Min MPa |
Tensile Strength | 500 - 700 MPa |
Elongation | 45 Min% |
INCONEL X-750
Chemical compositions and mechanical properties of INCONEL X-750.
Chemical compositions - INCONEL X-750
Element | Min | Max |
---|---|---|
Carbon | - | 0.08 |
Manganese | - | 0.3 |
Silicon | - | 0.5 |
Sulfer | - | 0.01 |
Nickel + Cobalt | 70.0 min | 70.0 min |
Chromium | 14 | 17 |
Iron | 5 | 9 |
Aluminum | 0.4 | 1 |
Titanium | 2.25 | 2.7 |
Copper | - | 0.5 |
Cb + Ta | 0.7 | 1.2 |
Mechanical properties - INCONEL X-750
Temper | Tensile Strength, | Yield Strength | Elongation | Hardness, |
---|---|---|---|---|
Temper | psi | 0.2% offset, psi | in 2", % | Brinell |
Hot-finished + 1300°F/20 hr,A.C | 170,000-206,000 | 120,000-163,000 | 25-15 | 313-400 |
Hot-finished + Annealed | - | - | - | - |
1800°F/1 hr, A.C + 1350°F/ | 162,000-193,000 | 115,000-142,000 | 30-15 | 300-390 |
8 hr, F.C. 100°F/hr to | - | - | - | - |
1150°F (total 18 hr), A.C. | - | - | - | - |
Hot-finished + 1625°F/24 hr, | 160,000-188,000 | 100,000-135,000 | 30-15 | 302-363 |
A.C + 1300°F/20 hr, A.C. | - | - | - | - |
Cold-rolled, annealed + | - | - | - | - |
1300°F/20 hr, A.C. | 160,000-197,000 | 105,000-150,000 | 30-20 | 300-400 |
ASTM A453 GRADE 660 (A/B/C/D)
Chemical compositions and mechanical properties of ASTM A453 GRADE 660 (A/B/C/D).
Chemical compositions - ASTM A453 GRADE 660 (A/B/C/D)
Elements | Content, % | Allowable Variation, Over or Under, % |
---|---|---|
Carbon | 0.08 max | 0.01 over |
Manganese | 2.00 max | 0.04 |
Phosphorus | 0.04 max | 0.005 over |
Sulfur | 0.03 max | 0.005 over |
Silicon | 1.00 max | 0.05 |
Nickel | 24.00 - 27.00 | 0.2 |
Chromium | 13.50 - 16.00 | 0.2 |
Molybdenum | 1.00 - 1.50 | 0.05 |
Titanium | 1.90 - 2.35 | 0.05 |
Aluminum | 0.35 max | 0.05 over |
Vanadium | 0.10 - 0.50 | 0.03 |
Boron | 0.001 - 0.010 | 0.0004 under to 0.001 over |
Mechanical properties - ASTM A453 GRADE 660 (A/B/C/D)
Tensile Class | Tensile Strength, min | Tensile Strength, min | Yield strength, 0.2% offset, min | Yield strength, 0.2% offset, min | Elongation in 4D min, % | Reduction of Area, min, % |
---|---|---|---|---|---|---|
ksi | MPa | ksi | MPa | |||
A, B and C | 130 | 895 | 85 | 585 | 15 | 18 |
D | 130 | 895 | 105 | 725 | 15 | 18 |
Mechanical properties (Hardness) - ASTM A453 GRADE 660 (A/B/C/D)
Tensile Class | Brinell Hardness Number | Approximate Rockwell Hardness B & C | Approximate Rockwell Hardness B & C |
---|---|---|---|
min | max | ||
A B and C | 248 - 341 | 24 HRC | 27 HRC |
D | 248 - 321 | 24 HRC | 35 HRC |
Mechanical properties (Stress rupture requirements) - ASTM A453 GRADE 660 (A/B/C/D)
Tensile Class | Test Temperature °F [°C] | Stress, min | Stress, min | Time to Rupture, min, h [Note] | Elongation, min, % |
---|---|---|---|---|---|
ksi | Mpa | ||||
A, B and C | 1200 [650] | 56 | 385 | 100 | 5 |
D | 1200 [650] | 40 | 275 | 100 | 5 |
HASTELLOY C22
Chemical compositions and mechanical properties for HASTELLOY C22.
Chemical Compositions - HASTELLOY C22
Limiting Chemical Composition, % | |
Nickel | Balance* |
Chromium | 20.0-22.5 |
Molybdenum | 12.5-14.5 |
Iron | 2.0-6.0 |
Tungsten | 2-3.5.5 |
Cobalt | 2.5 max. |
Vanadium | 0.35 max. |
Carbon | 0.015 max. |
Manganese | 0.50 max. |
Sulfur | 0.02 max. |
Silicon | 0.08 max |
Phosphorus | 0.02 max |
Mechanical properties - HASTELLOY C22
Ultimate Tensile | Yield Strength (0.2% OS) | Elong. in 2 in. (50.8mm) or 4D min., % | R/A | Hardness | |
---|---|---|---|---|---|
Min | 100 KSi | 45 KSi | 45 | - | - |
Max | - | - | - | - | - |
Min | 690 MPa | 310 MPa | - | - | - |
Max | - | - | - | - | - |
HASTELLOY C276
Chemical compositions and mechanical properties for HASTELLOY C276.
Chemical compositions - HASTELLOY C276
% | Ni | Cr | Mo | W | Co | C | Mn | Si | P | S | Fe | V |
---|---|---|---|---|---|---|---|---|---|---|---|---|
Min | Balance | 14.5 | 15 | 3 | 0 | 0 | 0 | 0 | 0 | 0 | 4 | 0 |
Max | Balance | 16.5 | 17 | 4.5 | 2.5 | 0.01 | 1 | 0.08 | 0.04 | 0.03 | 7 | 0.35 |
Mechanical properties - HASTELLOY C276
Mechanical & Physical Properties | 21⁰C | 100⁰C | 200⁰C | 300⁰C | 400⁰C |
---|---|---|---|---|---|
Ultimate Tensile Strength for sheet ≤ 5 mm thick | 750-1000 | ||||
Ultimate Tensile Strength for sheet 5 to ≤ 20 mm thick | 700-950 | ||||
Ultimate Tensile Strength for bar ≤ 90 mm thick | 700-950 | ||||
0.2% Yield Strength for sheet ≤ 50 mm thick | 280 | 240 | 220 | 195 | |
0.2% Yield Strength for sheet 5 to ≤ 20 mm thick | 255 | 225 | 200 | 170 | |
0.2% Yield Strength for bar ≤ 90 mm thick | 255 | 225 | 200 | 170 | |
Elongation, % for sheet ≤ 5 mm thick | 30 | ||||
Elongation, % for sheet 5 to ≤ 20 mm thick | 25 | ||||
Elongation, % for bar ≤ 90 mm thick | 35 | ||||
Charpy Impact V-notch mean value / J | 96 (56 when welded) | ||||
Charpy Impact V-notch indicidual value / J | 67 (39 when welded) |
HASTELLOY X
Chemical compositions and mechanical properties for HASTELLOY X.
Chemical compositions - HASTELLOY X
Element | Min | Max |
---|---|---|
Molybdenum | 8 | 10 |
Chromium | 20.5 | 23 |
Iron | 17 | 20 |
Tungsten | 0.2 | 1 |
Cobalt | 0.5 | 2.5 |
Carbon | 0.05 | 0.015 |
Silicon | - | 1 |
Manganese | - | 1 |
Boron | - | 0.01 |
Phosphorus | - | 0.04 |
Sulfur | - | 0.03 |
Nickel | Remainde | Remainde |
S31803
Chemical compositions and mechanical properties for S31803.
Chemical compositions - S31803
Chemical Element | % Present |
---|---|
Carbon (C) | 0.0 - 0.03 |
Chromium (Cr) | 21.00 - 23.00 |
Manganese (Mn) | 2.00 max |
Silicon (Si) | 1.00 max |
Phosphorous (P) | 0.0 - 0.03 |
Sulphur (S) | 0.0 - 0.02 |
Nickel (Ni) | 4.50 - 6.50 |
Nitrogen (N) | 0.08 - 0.20 |
Molybdenum (Mo) | 2.50 - 3.50 |
Iron (Fe) | Balance |
Mechanical properties - S31803
Mechanical Property | Value |
---|---|
Proof Stress | 450 Min MPa |
Tensile Strength | 620 Min MPa |
Elongation A50 mm | 25 Min % |
Hardness Brinell | 290 Max HB |
S32750
Chemical compositions and mechanical properties for S32750.
Chemical compositions - S32750
Weight % | C | Si | Mn | S | P | Cr | Ni | Mo | Cu | N |
---|---|---|---|---|---|---|---|---|---|---|
Min | 24,0 | 6,00 | 3,00 | 0,24 | ||||||
Max | 0,03 | 0,80 | 1,20 | 0,020 | 0,035 | 26,0 | 8,00 | 5,00 | 0,50 | 0,32 |
Mechanical properties - S32750
Yield strength Rp0.2, | Tensile strength Rm, | Elongation | Hardness | Impact, Charpy-V, -46ºC | Pre | |
---|---|---|---|---|---|---|
BAR | ≥ 550 | ≥ 750 | ≥ 25 | ≤ 310 | ≥ 45 | ≥ 40 |
S31254 / 254SMO
Chemical compositions and mechanical properties for S31254 / 254SMO.
Chemical compositions - S31254 / 254SMO
Melting Point | Density | Specific Gravity | Modulus of Elasticity |
---|---|---|---|
in Tension | |||
1320-1390 ℃ | 8.0 g/cm3 | 7.8 | 195 GPa |
Mechanical properties - S31254 / 254SMO
Alloy | Tensile Strength | Yield Strength | % Elongation |
---|---|---|---|
Minimum (psi) | Minimum 0.2% offset (psi) | in 2" Minimum | |
254SMO | 98600 | 43500 | 50 |
Mechanical properties - S31254 / 254SMO
Alloy | C | Si | Mn | P | S | Cr | Ni | Mo | Cu | N |
---|---|---|---|---|---|---|---|---|---|---|
254SMO | 0.02 | 0.8 | 1 | 0.03 | 0.01 | 20 | 18 | 6.1 | 0.7 | 0.2 |
MONEL 400
Chemical compositions and mechanical properties for MONEL 400.
Chemical compositions - MONEL 400
Ni | C | Mn | S | Si | Cu | Fe | |
---|---|---|---|---|---|---|---|
Min | 0.3 | 2 | 0.024 | 0.5 | 34 | 2.5 | |
Max | 63 | 28 |
Mechanical properties - MONEL 400
Ultimate Tensile | Yield Strength (0.2% OS) | Elong. in 2 in. or 50mm (or 4D), min.,% | R/A | Hardness | |
---|---|---|---|---|---|
Cold Worked/SR | |||||
Min | 87 KSi | 60 KSi | 20B | ||
Max | |||||
Min | 600 MPa | 415 MPa | |||
Max | |||||
Hot Worked/SR | |||||
Min | 80 KSi | 40 KSi | 30D | ||
Max | |||||
Min | 552 MPa | 276 MPa | |||
Max |
MONEL K500
Chemical compositions and mechanical properties for MONEL K500.
Chemical compositions - MONEL K500
Chemical Composition of Monel K500, % | |
Nickel | ≥63.0 |
Copper | 27.0-33.0 |
Aluminum | 2.30-3.15 |
Titanium | 0.35-0.85 |
Carbon | ≤0.25 |
Manganese | ≤1.50 |
Iron | ≤2.0 |
Sulfur | ≤0.01 |
Silicon | ≤0.50 |
Mechanical properties - MONEL K500
Tensile Strength, min. | Tensile Strength, min. | Yield Strength, min. | Yield Strength, min. | Elongation, min. | Hardness, min. |
---|---|---|---|---|---|
Mpa | ksi | Mpa | ksi | % | HB |
1100 | 160 | 790 | 115 | 20 | 300 |
INCOLOY 800
Chemical compositions and mechanical properties for INCOLOY 800.
Chemical compositions - INCOLOY 800
Ni | Fe | Cr | Mb | Cu | Ti | C | Mn | S | SI | AI |
---|---|---|---|---|---|---|---|---|---|---|
38.0-46.0 | 22.0 min | 19.5-23.5 | 2.5-3.5 | 1.5-3.0 | .6-1.2 | 0.05 max | 1.0 max | 0.3 max | 0.5 max | 0.2 max |
Mechanical properties - INCOLOY 800
Tensile (ksi) | .2% Yield (ksi) |
---|---|
85 | 30-35 |
INCOLOY 925
Chemical compositions and mechanical properties for INCOLOY 925.
Chemical compositions - INCOLOY 925
C | Si | Mn | P | S | Cr | Ni | Mo | Cu | NbCbTa | Ti | Al | Fe | |
---|---|---|---|---|---|---|---|---|---|---|---|---|---|
Min | 19.5 | 42 | 2.5 | 1.5 | 1.9 | 0.1 | 22 | ||||||
Max | 0.03 | 0.5 | 1 | 0.03 | 0.03 | 22.5 | 46 | 3.5 | 3 | 0.5 | 2.4 | 2.4 | 0 |
Mechanical properties - INCOLOY 925
U.T.S | 140 KSI Min | (965 N/mm2) |
---|---|---|
0.2% Proof Stress | 110 KSI Min | (758 N/mm2) |
Elongation | 20% | |
Red of Area | 20% | |
CVN Impacts @ -60°C (-75°F) | 47 Joules | (35 ft-lbf) |
NACE MR0175 limits the hardness to 38 HRC max. |
17-4 PH
Chemical compositions and mechanical properties for 17-4 PH.
Chemical compositions - 17-4 PH
Alloy | C | Si | Mn | P | Cr | Ni | S | Nb | Cu |
---|---|---|---|---|---|---|---|---|---|
17-4 PH | 0.07 | 1 | 1 | 0.04 | 15.0-17.5 | 3.0-5.0 | 0.03 | 0.15-0.45 | 3.0-5.0 |
Mechanical properties - 17-4 PH
Melting Point | Density | Modulus of Elasticity |
---|---|---|
in Tension | ||
1404 - 1440 ℃ | 7.75g/cm3 | 190-210 GPa |
Mechanical properties - 17-4 PH
Alloy | Tensile Strength | Yield Strength | % Elongation |
---|---|---|---|
Minimum (psi) | Minimum 0.2% offset (psi) | in 2" Minimum | |
17-4 PH | 160,00 | 145000 | 5 |
Free, No-Obligation Quote
Get in touch and let us know your requirements. A member of our specialist team will be in touch with a bespoke quote at the right price.
Prefer to call? Get in touch directly: